Détails
LINCORE® 102W provides a tool steel deposit that retains hardness at high working temperatures produce chromium, molybdenum and tungsten chemical composition to be used with recommended Lincoln weld® 802 and Lincoln weld® 860 standard flux for semiautomatic operations.
Traits
- Metal-cored wire which produces a tool steel deposit that retains hardness at high working temperatures
- Used for guide rolls and work rolls
- Can also be used as the seat on blast furnace bells and hoppers
- Primary Recommended Flux: 802
- Secondary Recommended Flux: 801
Applications typiques
- Work rolls
- Metal-to-metal sliding wear (where minimal or no lubrication is present)
Positions de soudage
- N/A
Gaz de protection
- N/A
Disclaimers
Des informations de service
Vous pourriez également avoir besoin
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 802® | Typical Result | 48-54 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Mo | %Si | %V | %W |
|---|---|---|---|---|---|---|---|---|
| Lincolnweld® 802® | Typical Result | 0.28 | 6.5 | 1.5 | 1.0 | 0.4 | 0.15 | 1.0 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 240 |
| 3/32 in (2.4 mm) | DC+ | 3.0 (120) | 28 | 400 |
| 3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 500 |
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 390 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 540 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 680 |
| 5/32 in (4.0 mm) | DC+ | 1.4 (55) | 27 | 500 |
| 5/32 in (4.0 mm) | DC+ | 2.2 (85) | 30 | 685 |
| 5/32 in (4.0 mm) | DC+ | 2.9 (115) | 32 | 850 |