Sarma tubulara cu pulberi cu auto-protectie (FCAW-S)

CLASIFICARI:
EN ISO : T Fe9

LINCORE® 15CRMN Wire for spreader cones, crusher hammers, and manganese parts. Use as a build-up layer before capping with abrasion-resistant alloys.

Partener de afaceri Lincoln Electric?

Conectați-vă pentru a vedea prețul

DETALII

LINCORE® 15CRMN provides an austenitic manganese deposit which exhibits very good crack resistance ideal for open arc mode for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel offers unlimited layers with proper preheat and interpass temperatures and procedures.

Caracteristici

Poate fi utilizata cu arc descoperit pentru imbinarile dintre otel manganos cu otel carbon, otel slab aliat, austenitic sau otel inoxidabil
Straturi nelimitate, cu proceduri adecvate pentru temperaturile de preincalzire si intre straturi
Poate fi folosit ca strat tampon inainte de placarea cu consumabile cu rezistenta la abraziune
Unlimited layers with proper preheat and interpass temperatures and procedures

Aplicații tipice

Bara, Galeata, Zdrobitor, Lame
Tragator, Draga, Ciocan, Mixer / Amestecator
Vetre deschise, Placi, Generatoare de energie, Pompe, Cai de rulare
Role, Ecrane, Lopeti, Dinti, Roti

Poziții de sudare

La masa / Orizontal

Informații despre service

Documentație

Fisa tehnica Lincore® 15CrMn

S-ar putea să aveți nevoie și de

Pistol de sudare K126® Classic® Innershield® 350A FCAW-SS 10 ft 062-332

K126-1

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Pagina de căutare FDS

MECHANICAL PROPERTIES

Classification	Hardness Rockwell C
Typical Result	18-22
Typical Result, Work-hardened	45-50

DEPOSIT COMPOSITION

Classification	%C	%Cr	%Mn	%Si
Typical Result	0.4	16.0	15.0	0.2

TYPICAL OPERATING PROCEDURES

Diameter	Polarity	ESO mm (in.)	Wire Feed Speed m/min (in/min)	Voltage volts	Approx. Current amps	Deposition Rate kg/hr (lb/hr)
5/64 in (2.0 mm)	DC+	32 (1 1/4)	3.2 (125)	26	210	3.3 (7.3)
5/64 in (2.0 mm)	DC+	32 (1 1/4)	5.1 (200)	29	280	5.3 (11.7)
5/64 in (2.0 mm)	DC+	32 (1 1/4)	6.4 (250)	30	320	6.8 (15.1)
5/64 in (2.0 mm)	DC+	32 (1 1/4)	8.9 (350)	32	380	9.7 (21.3)
7/64 in (2.8 mm)	DC+	45 (1 3/4)	1.9 (75)	26	250	2.5 (5.5)
7/64 in (2.8 mm)	DC+	45 (1 3/4)	3.2 (125)	28	320	5.1 (11.3)
7/64 in (2.8 mm)	DC+	45 (1 3/4)	3.8 (150)	29	350	6.6 (14.6)
7/64 in (2.8 mm)	DC+	45 (1 3/4)	4.4 (175)	30	380	7.5 (16.4)
7/64 in (2.8 mm)	DC+	64 (2 1/2)	3.8 (150)	30	320	6.7 (14.9)
7/64 in (2.8 mm)	DC+	64 (2 1/2)	5.1 (200)	33	390	8.7 (19.2)
7/64 in (2.8 mm)	DC+	64 (2 1/2)	5.7 (225)	34	410	9.8 (21.7)
7/64 in (2.8 mm)	DC+	64 (2 1/2)	6.4 (250)	35	425	11.4 (25.1)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.