LINCORE® M ideal for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels, deposits resistance on severe impact as well as moderate abrasion and offers unlimited layers with proper preheat and interpass temperatures and procedures.
Caracteristici
- Recomandat pentru realizarea suprafetelor dure si repararea materialelor austenitice manganoase tip Hasfield precum si a otelurilor carbon si slab aliate
- Straturi nelimitate, cu proceduri adecvate pentru temperaturile de preincalzire si intre straturi
- Depunerile rezistente la impact puternice precum si la abraziune moderata.
- Unlimited layers with proper preheat and interpass temperatures and procedures
Aplicații tipice
- Bara, Galeata, Zdrobitor, Lama, Draga, Glisiere
- Ciocan, Moara, Mixer, Vatra cuptor, Table
- Generatoare de putere, Pompe, Cai de rulare, Role
- Ecran, Lopeti, Dinti, Roti
- Buckets
Poziții de sudare
- La masa / Orizontal
Informații despre service
Documentație
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Pagina de căutare FDS
MECHANICAL PROPERTIES
| Classification | Hardness Rockwell C |
|---|---|
| Typical Result | 18-28 |
| Typical Result, Work-hardened | 30-48 |
DEPOSIT COMPOSITION
| Classification | %C | %Cr | %Mn | %Ni | %Si |
|---|---|---|---|---|---|
| Typical Result | 0.6 | 4.9 | 13.0 | 0.5 | 0.4 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
ESO
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
Deposition Rate
kg/hr (lb/hr) |
|---|---|---|---|---|---|---|
| 0.045 in (1.1 mm) | DC+ | 25 (1) | 5.1 (200) | 22 | 80 | 1.5 (3.3) |
| 0.045 in (1.1 mm) | DC+ | 25 (1) | 8.9 (350) | 24 | 145 | 2.7 (6.0) |
| 0.045 in (1.1 mm) | DC+ | 25 (1) | 12.7 (500) | 26 | 185 | 4.4 (9.6) |
| 1/16 in (1.6 mm) | DC+ | 30 (1 1/8) | 3.8 (150) | 23 | 130 | 2.2 (4.9) |
| 1/16 in (1.6 mm) | DC+ | 30 (1 1/8) | 6.4 (250) | 25 | 200 | 3.9 (8.6) |
| 1/16 in (1.6 mm) | DC+ | 30 (1 1/8) | 8.9 (350) | 27 | 250 | 5.6 (12.4) |
| 5/64 in (2.0 mm) | DC+ | 32 (1 1/4) | 3.2 (125) | 24 | 240 | 2.9 (6.4) |
| 5/64 in (2.0 mm) | DC+ | 32 (1 1/4) | 4.4 (175) | 27 | 300 | 4.2 (9.3) |
| 5/64 in (2.0 mm) | DC+ | 32 (1 1/4) | 6.4 (250) | 29 | 360 | 6.2 (13.6) |
| 7/64 in (2.8 mm) | DC+ | 45 (1 3/4) | 1.9 (75) | 25 | 240 | 3.5 (7.8) |
| 7/64 in (2.8 mm) | DC+ | 45 (1 3/4) | 3.2 (125) | 27 | 360 | 6.2 (13.6) |
| 7/64 in (2.8 mm) | DC+ | 45 (1 3/4) | 3.8 (150) | 28 | 395 | 7.5 (16.6) |
| 7/64 in (2.8 mm) | DC+ | 64 (2 1/2) | 1.9 (75) | 25 | 240 | 3.6 (8.0) |
| 7/64 in (2.8 mm) | DC+ | 64 (2 1/2) | 4.4 (175) | 30 | 400 | 8.8 (19.5) |
| 7/64 in (2.8 mm) | DC+ | 64 (2 1/2) | 5.7 (225) | 32 | 455 | 11.6 (25.6) |
NOTES
| Note |
|---|
| As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum. |
| A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese. |