Lincolnweld® 860®

Submerged Arc Welding (SAW) | BRE00860S25

FLUX 860 - 25 KG PE BAG

Diameter

Select Diameter

  • Flux

Package

Select Package

  • 22.7 KG BAG
  • 25 KG PE BAG

DETAILS

Industry standard for submerged arc welding applications.Excellent operating characteristics in a variety of general welding applications. Capable of producing weld deposits with impact toughness exceeding 27 J at -40degC with L-61 wire

Features

  • Industry standard for submerged arc welding applications
  • Excellent operating characteristics in a variety of general welding applications.
  • Capable of producing weld deposits with impact toughness exceeding 27 J at -40degC with L-61 wire

Service Information

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Wire Classification Postweld Heat Treatment Yield Strength @ 0.2% Offset
MPa (ksi) 		Tensile Strength
MPa (ksi) 		Elongation
% 		Charpy V-Notch
J (ft-lbs) @ -30°C (-20°F) 		Charpy V-Notch
J (ft-lbs) @ -40°C (-40°F) 		Charpy V-Notch
J (ft-lbs) @ -45°C (-50°F) 		Charpy V-Notch
J (ft-lbs) @ -50°C (-60°F)
Lincolnweld® L-50® F7A2-EM13K-H4 As-welded 420 (61) 540 (78) 30 88 (65)
Lincolnweld® L-56® F7A2-EH11K-H4 As-welded 500 (72) 610 (88) 28 75 (55)
Lincolnweld® L-56® F7P2-EH11K-H4 1 hour @ 620°C (1150°F) 430 (62) 560 (81) 31 96 (71)
Lincolnweld® L-60 F6A2-EL12-H4 As-welded 370 (54) 440 (64) 33 198 (146)
Lincolnweld® L-61® F6P5-EM12K-H8 1 hour @ 620°C (1150°F) 370 (53) 480 (69) 35 148 (109)
Lincolnweld® L-61® F7A4-EM12K-H8 As-welded 420 (61) 510 (74) 30 145 (107)
Lincolnweld® L-70 F7A2-EA1-A2-H4 As-welded 470 (68) 560 (81) 28 96 (71)
Lincolnweld® L-70 F7P2-EA1-A2-H4 1 hour @ 620°C (1150°F) 440 (64) 540 (78) 29 94 (69)
Lincolnweld® LA-71 F7A2-EM14K-H4 As-welded 460 (67) 560 (81) 30 145 (107)
Lincolnweld® LA-71 F7P2-EM14K-H4 1 hour @ 620°C (1150°F) 420 (61) 540 (78) 30 123 (91)
Lincolnweld® LA-75 F7A2-ENi1K-Ni1-H4 As-welded 470 (68) 570 (82) 29 115 (85)
Lincolnweld® LA-75 F7P2-ENi1K-Ni1-H4 1 hour @ 620°C (1150°F) 410 (60) 530 (77) 31 123 (91)
Lincolnweld® LA-81 (LNS 140TB) F9TA6G-EA2TiB As-welded 610 (88) 670 (97) 27 33 (24)
Lincolnweld® LA-85 (LNS 165) F8A4-ENi5-Ni5-H4 As-welded 490 (71) 580 (84) 27 119 (88)
Lincolnweld® L-S3 (LNS133U,L50M) F7A2-EH12K-H4 As-welded 420 (61) 520 (75) 30 138 (102)
Pipeliner® LA-85 F8A4-ENi5-Ni5-H4 As-welded 490 (71) 580 (84) 27 119 (88)

DEPOSIT COMPOSITION

Wire Classification %B %C %Cr %Cu %Mn %Mo %Ni %P %S %Si %Ti %Ti+V+Zr Diffusible Hydrogen
mL/100g Weld Metal
Lincolnweld® L-50® F7A2-EM13K-H4 0.04 0.09 1.74 0.014 0.009 0.54 3
Lincolnweld® L-56® F7A2-EH11K-H4 0.05 0.09 2.12 0.018 0.004 0.86 2
Lincolnweld® L-56® F7P2-EH11K-H4 0.05 0.09 2.12 0.018 0.040 0.86 2
Lincolnweld® L-60 F6A2-EL12-H4 0.04 0.07 1.04 0.016 0.010 0.25 4
Lincolnweld® L-61® F6P5-EM12K-H8 0.05 0.06 1.52 0.018 0.010 0.36 2
Lincolnweld® L-61® F7A4-EM12K-H8 0.05 0.06 1.52 0.018 0.009 0.35 2
Lincolnweld® L-70 F7A2-EA1-A2-H4 0.04 0.08 1.31 0.52 0.015 0.009 0.28 3
Lincolnweld® L-70 F7P2-EA1-A2-H4 0.05 0.08 1.28 0.53 0.015 0.009 0.26 3
Lincolnweld® LA-71 F7A2-EM14K-H4 0.05 0.13 1.76 0.016 0.008 0.57 0.020 3
Lincolnweld® LA-71 F7P2-EM14K-H4 0.05 0.13 1.74 0.016 0.009 0.06 0.020 3
Lincolnweld® LA-75 F7A2-ENi1K-Ni1-H4 0.05 0.03 0.10 1.64 0.01 0.86 0.014 0.009 0.63 0.01 2
Lincolnweld® LA-75 F7P2-ENi1K-Ni1-H4 0.05 0.03 0.10 1.68 0.00 0.86 0.014 0.010 0.61 0.01 2
Lincolnweld® LA-81 (LNS 140TB) F9TA6G-EA2TiB 0.0037 0.06 0.15 1.35 0.21 0.011 0.004 0.31 0.032
Lincolnweld® LA-85 (LNS 165) F8A4-ENi5-Ni5-H4 0.04 0.08 1.58 0.22 0.87 0.020 0.003 0.30 3
Lincolnweld® L-S3 (LNS133U,L50M) F7A2-EH12K-H4 0.05 0.10 1.77 0.015 0.009 0.45 3
Pipeliner® LA-85 F8A4-ENi5-Ni5-H4 0.04 0.08 1.58 0.22 0.87 0.020 0.003 0.30 3

FLUX COMPOSITION

Classification %Al2O3 %CaF2 %CaO %MgO %MnO %Na2O %SiO2 %TiO2 %ZrO2 %Metal Alloys
Typical Result 30 13 2 18 11 2 19 2 0 3