DETAILS
LINCORE® 4130 is ideal for rebuilding worn parts to near final dimensions before applying final hardfacing layer with recommended Lincolnweld® 801, 802 and Lincoln weld 880 standard flux for semiautomatic operations.
Features
- Metal-cored wire for general build-up
- Can be flame hardened to 38 Rockwell C (RC)
- Used on mining components such as cable drums, sheaves, gears and shafts
Disclaimers
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 801® | Typical Result | 17-21 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Mo | %Si |
|---|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.12 | 0.8 | 1.1 | 0.2 | 0.3 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 300 |
| 3/32 in (2.4 mm) | DC+ | 3.0 (120) | 28 | 410 |
| 3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 520 |
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 350 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 465 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 590 |