Metalshield® HDT™ is a high deposition metal core used in conjunction with Lincoln Electric’s Process HDT high deposition waveform. This innovative solution delivers single wire deposition rates of up to 40 lbs/hour all while maintaining stable arc conditions and consistency in weldability.
Features
- High deposition metal core wire used in conjunction with Lincoln Electric’s Process HDT high deposition waveform process solution
- Delivers single wire deposition rates up to 40 lbs/hour
- Designed specifically for high amperage applications to help increase productivity while maintaining stable arc conditions
- Consistent, uniform penetration with excellent toe wetting producing robust weld profiles
- Specially formulated to resist porosity and nitrogen pick up when applied as noted
- Excellent operation on mill scale
- H4 diffusible hydrogen level
- It is recommended to test and verify Metalshield HDT procedures prior to use in intended application.
- Contact your local Lincoln Electric representative and Lincoln Electric Application Resource Center for assistance.
Disclaimers
Service Information
Documentation
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
| CONFORMANCES | SPECIFICATION | CLASSIFICATION |
|---|---|---|
| AWS | AWS A5.18 | E70C-GM-H4 |
| ASME | ASME SFA-A5.18 | E70C-GM-H4 |
MECHANICAL PROPERTIES
| Classification | Shielding Gas |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -29°C (-20°F) |
|---|---|---|---|---|---|
| E70C-GM-H4 | 400 (58) min. | 480 (70) min. | 22 min. | 27 (20) min. | |
| Typical Result, As-welded | 75% Ar, 25% CO2 | 606 (88) | 724 (105) | 25 | 68 (50) |
DEPOSIT COMPOSITION
| Classification | Shielding Gas | %C | %Mn | %Si | %S | %P | %Cu | %Ni | %Cr | %Mo | %V |
Diffusible Hydrogen
mL/100g Weld Metal |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| E70C-GM-H4 | Not Specified | Not Specified | Not Specified | Not Specified | Not Specified | Not Specified | Not Specified | Not Specified | Not Specified | Not Specified | Not Specified | |
| Typical Result | 75% Ar, 25% CO2 | 0.07 | 2.4 | 1.1 | 0.01 | 0.01 | 0.05 | 0.02 | 0.04 | ≤ 0.01 | ≤ 0.01 | 1-2 |
TYPICAL OPERATING PROCEDURES
| Diameter in (mm) | Polarity | Shielding Gas | CTWD⁽¹⁾ mm (in) | Wire Feed Speed m/min (in/min) | Voltage (volts) | Current (amps) | Melt-Off Rate kg/hr (lb/hr) | Deposition Rate kg/hr (lb/hr) | Efficiency (%) |
|---|---|---|---|---|---|---|---|---|---|
| 1/16 (1.6) | DC+ | 80% Ar, 20% CO2 | 25.4 (1) | 10.2 (400) | 36 | 440 | 8.7 (19.2) | 8.3 (18.3) | 95 |
| 1/16 (1.6) | DC+ | 80% Ar, 20% CO2 | 25.4 (1) | 12.7 (500) | 37 | 510 | 10.8 (23.8) | 10.4 (22.9) | 96 |
| 1/16 (1.6) | DC+ | 80% Ar, 20% CO2 | 25.4 (1) | 15.2 (600) | 38 | 570 | 12.7 (27.9) | 12.3 (27.1) | 97 |
| 1/16 (1.6) | DC+ | 80% Ar, 20% CO2 | 28.6 (1-1/8) | 17.8 (700) | 42 | 565 | 14.9 (32.9) | 14.1 (31.2) | 95 |
| 1/16 (1.6) | DC+ | 80% Ar, 20% CO2 | 28.6 (1-1/8) | 20.3 (800) | 43 | 600 | 17.2 (37.9) | 16.5 (36.3) | 96 |
| 1/16 (1.6) | DC+ | 80% Ar, 20% CO2 | 28.6 (1-1/8) | 22.9 (900) | 44 | 645 | 19.1 (42.0) | 18.3 (40.3) | 96 |
NOTES
| Name |
|---|
| ⁽¹⁾ To estimate ESO, subtract 3/16 in (4.8 mm) from CTWD. |
| NOTE: The listed procedures were welded with HDT mode. |