DETAILS
Metalshield® MC®-110 from Lincoln Electric is a low alloy metal cored wire capable of producing welds with tensile strengths of 760 MPa (110 ksi).
Features
- H4 diffusible hydrogen levels
- Low spatter and excellent arc stability
- Deoxidizing agents minimize pre- and post-weld clean up
- Enhanced silicon island management
- Low temperature impact properties - charpy V-notch test results capable of exceeding 40 J (30 ft·lbf) at -51°C (-60°F)
- Excellent bead shape and profile
Disclaimers
Service Information
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
| CONFORMANCES | SPECIFICATION | CLASSIFICATION |
|---|---|---|
| AWS | AWS A5.28 | E110C-K4-H4 |
| AWS | AWS A5.36 | E110T15-M20A6-K4-H4, E110T15-M21A6-K4-H4 |
| CWB | CWB/CSA | E110C-K4 H4 |
| ISO | ISO | T76 6 T15-0 M A-N4C1M2 H5 |
MECHANICAL PROPERTIES
| Classification | Shielding Gas |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -40°C (-40°F) |
Charpy V-Notch
J (ft-lbs) @ -51°C (-60°F) |
|---|---|---|---|---|---|---|
| E110C-K4-H4 | 680 (98) min. | 760 (110) min. | 15 min. | Not Specified | 27 (20) min. | |
| E110T15-M20A6-K4-H4 Requirement | 680 (98) min. | 760-900 (110-130) | 15 min. | Not Specified | 27 (20) min. | |
| Typical Result, As-welded | 75% Ar, 25% CO2 | 690-795 (100-115) | 760-825 (110-120) | 20-24 | 60-88 (44-65) | 45-80 (34-59) |
| Typical Result, As-welded | 90% Ar, 10% CO2 | 725-825 (105-120) | 790-895 (115-130) | 18-23 | 66-95 (48-70) | 59-82 (44-61) |
DEPOSIT COMPOSITION
| Classification | Shielding Gas | %C | %Mn | %Si | %S | %P | %Cu | %Ni | %Cr | %Mo | %V |
Diffusible Hydrogen
mL/100g Weld Metal |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| E110C-K4-H4 Requirement | 0.15 max. | 0.75-2.25 | 0.80 max. | 0.025 max. | 0.025 max. | 0.35 max. | 0.50-2.50 | 0.15-0.65 | 0.25-0.65 | 0.03 max. | 4.0 max. | |
| E110T15-M20A6-K4-H4 Requirement | 0.15 max. | 1.20-2.25 | 0.80 max. | 0.030 max. | 0.030 max. | Not Specified | 1.75-2.60 | 0.20-0.60 | 0.25-0.65 | 0.03 max. | 4 max. | |
| Typical Result | 75% Ar, 25% CO2 | 0.05-0.08 | 1.45-1.75 | 0.45-0.65 | 0.01-0.02 | 0.01-0.02 | 0.02-0.06 | 2.00-2.20 | 0.20-0.35 | 0.45-0.55 | 0.01-0.02 | 2.5-4 |
| Typical Result | 90% Ar, 10% CO2 | 0.05-0.08 | 1.45-1.75 | 0.45-0.65 | 0.01-0.02 | 0.01-0.02 | 0.02-0.06 | 2.00-2.20 | 0.20-0.35 | 0.45-0.55 | 0.01-0.02 | 2.5-4 |
TYPICAL OPERATING PROCEDURES
| Diameter in (mm) | Polarity | Shielding Gas | CTWD⁽¹⁾ mm (in) | Wire Feed Speed m/min (in/min) | Voltage (volts) | Current (amps) | Melt-Off Rate kg/hr (lb/hr) | Deposition Rate kg/hr (lb/hr) | Efficiency (%) |
|---|---|---|---|---|---|---|---|---|---|
| 0.045 (1.1) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 5.1 (200) | 22-24 | 170 | 2.4 (5.3) | 2.2 (4.7) | 88 |
| 0.045 (1.1) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 6.4 (250) | 24-26 | 190 | 3.0 (6.7) | 2.8 (6.1) | 91 |
| 0.045 (1.1) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 8.9 (350) | 26-28 | 240 | 4.2 (9.2) | 3.8 (8.4) | 91 |
| 0.045 (1.1) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 11.4 (450) | 28-30 | 290 | 5.4 (11.8) | 5.1 (11.3) | 95 |
| 0.045 (1.1) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 14.0 (550) | 30-32 | 330 | 6.5 (14.4) | 6.3 (13.9) | 97 |
| 0.045 (1.1) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 16.6 (650) | 31-33 | 370 | 7.8 (17.1) | 7.6 (16.7) | 97 |
| 0.052 (1.3) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 5.1 (200) | 23-25 | 225 | 3.2 (7.0) | 2.8 (6.2) | 89 |
| 0.052 (1.3) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1)) | 6.4 (250) | 25-27 | 255 | 4.0 (8.8) | 3.7 (8.1) | 92 |
| 0.052 (1.3) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 8.9 (350) | 27-29 | 295 | 5.5 (12.2) | 5.3 (11.6) | 95 |
| 0.052 (1.3) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 11.4 (450) | 29-31 | 350 | 7.2 (15.8) | 7.0 (15.4) | 98 |
| 0.052 (1.3) | DC+ | 90% Ar, 10% CO2 | 19-25 (3/4-1) | 14.0 (550) | 30-32 | 400 | 8.7 (19.1) | 8.5 (18.8) | 98 |
| 1/16 (1.6) | DC+ | 90% Ar, 10% CO2 | 25-32 (1-1 1/4) | 5.1 (200) | 24-26 | 270 | 4.4 (9.6) | 3.9 (8.6) | 89 |
| 1/16 (1.6) | DC+ | 90% Ar, 10% CO2 | 25-32 (1-1 1/4) | 6.4 (250) | 26-28 | 320 | 5.4 (12.1) | 5.1 (11.3) | 94 |
| 1/16 (1.6) | DC+ | 90% Ar, 10% CO2 | 25-32 (1-1 1/4) | 8.9 (350) | 28-30 | 385 | 7.7 (16.9) | 7.4 (16.4) | 97 |
| 1/16 (1.6) | DC+ | 90% Ar, 10% CO2 | 25-32 (1-1 1/4) | 11.4 (450) | 30-32 | 465 | 9.8 (21.6) | 9.6 (21.2) | 98 |
NOTES
| Name |
|---|
| ⁽¹⁾ To estimate ESO, subtract 3/16 in (4.8 mm) from CTWD. |
| NOTE: Consult steel manufacturer’s recommendations regarding minimum and maximum pre-heat temperature, interpass temperature, and heat input. |